MD MIX aluminium repair putty 2K, 115 g
Epoxy resin filled with aluminum.
For quick repairs of transmission housings, professional engine builds and boats.
Technical data:
Color: Aluminum
Pot life: 3-4 minutes
Mixing ratio: 1:1
Hardening time (depending on temperature): 8-10 minutes Full strength: after 24 hours
Operating temperature: +10 °C to +30 °C
Polymerization temperature: from +6 °C to +30 °C
Shear strength (DIN 53283): 4.5 N/mm² Shore D hardness: 87
Temperature resistance: -50°C to +180°C (short term +300°C)
Shrinkage: approx. 0.05% MD-MIX repairs bad holes, cracks and broken threads in metal, wood and plastic.
Fills cracks and holes Resistant to temperatures up to +180 °C and for short periods up to +300 °C
For on-site repairs Easy to use, the material is worked like plasticine Extremely high Shore hardness D of 87 (concrete 60) It can be machined mechanically
Epoxy resin filled with aluminum.
For quick repairs of transmission housings, professional engine builds and boats.
Technical data:
Color: Aluminum
Pot life: 3-4 minutes
Mixing ratio: 1:1
Hardening time (depending on temperature): 8-10 minutes Full strength: after 24 hours
Operating temperature: +10 °C to +30 °C
Polymerization temperature: from +6 °C to +30 °C
Shear strength (DIN 53283): 4.5 N/mm² Shore D hardness: 87
Temperature resistance: -50°C to +180°C (short term +300°C)
Shrinkage: approx. 0.05% MD-MIX repairs bad holes, cracks and broken threads in metal, wood and plastic.
Fills cracks and holes Resistant to temperatures up to +180 °C and for short periods up to +300 °C
For on-site repairs Easy to use, the material is worked like plasticine Extremely high Shore hardness D of 87 (concrete 60) It can be machined mechanically