Epoxy Resin-Lamination L+CL - 3.25 kg.

The Epoxy Resin L + Hardener CL resin system offers superior impregnating and wetting properties towards carbon, glass, aramid and natural fibres.

It is especially suitable for carbon coating of automobile parts.

-Low viscosity
-High UV stability
-Hardening even of thin layers
-Glass transition temperature (Tg) > 90°C (post-curing at 70°C/15 h)
-High static and dynamic resistance (equal to Epoxy Resin L 285 with Hardener 285)
-Free from nonylphenol and DETA

Processing time: 60 minutes (100 g / 20 ° C)

Mixing ratio:
100: 30 parts by weight resin: hardener
100: 35 parts by volume resin: hardener

The resin system is environmentally polymerized and does not develop distinctive brittleness even at polymerization temperatures below 20 °C (for at least 48 h). However, to improve the physical and chemical properties, it is recommended to carry out a post polymerization at least at 40 °C for over 15 h.

It has an excellent price/performance ratio and is suitable for the following processes:

-Hand lamination
-Vacuum molding
-Pressure molding

Pot Life 60 min 20°

Complete catalysis 24H

Mixing ratio 100:30 by weight

3.25 kg pack.